CPS strong reaction cross laminated film sticky adhesive waterproofing membrane prices I. Introduction 1. Introduction CPS strong reaction cross laminated film stick self-adhesive waterproof membrane is polyethylene-based materials, the addition of antioxidants, light stabilizers agents, anti-aging materials such as mother, the upper and lower surfaces of high strength polypropylene non-woven composite, after a three-roll hot extrusion composite made of waterproof membrane. 2.1 Features 1) water impermeability ability. 2) high tensile strength, strong deformation adaptability, good low temperature flexibility to adapt to a wide temperature range. 3) soft, comes with good, simple construction, and grass-roots firmly bonded. 4) long life, resistance to chemical corrosion, anti-aging, non-toxic. 2.2 Scope For waterproof roofing and underground construction projects, water conservancy, environmental protection, metallurgy, chemical and plant and other projects, seepage, separated steam. Second, the design points 1. General Provisions 1) CPS strong reaction cross laminated film adhesive stick waterproofing membrane waterproof fortification levels according to project requirements, the use of one or more layers. 2) when the roof, underground, water conservancy, environmental protection, metallurgy, chemical industry, tunnels and other water projects applied to meet the requirements of the relevant standards. 2. Points 2.1 Construction Construction grassroots acceptance procedures (screed) → cleaning grassroots (screed) → Preparation → complex parts of cement bonded material waterproof membrane Stones → → lap joint and complex parts of the sealed waterproof layer → acceptance → protective layer construction → conservation three, primary requirement 1) CPS strong reaction sticky membrane waterproofing layer substrate should be solid, clean, smooth, non-porous, free from sand and cracks, moisture content of 30% to 50% is appropriate. Yang angle should do an arc or knuckle. 2) primary treatment agent should be compatible with the web and adhesive material, brushing must be uniform, do not open at the end, do not accumulate, dry surface after the start paving waterproofing membrane. 3) Construction of the ambient temperature should be in the range of 5 ~ 28 ℃, below 0 ℃ prohibit construction, wind should be in the following four. Paste the four coils, order and direction paving waterproofing membrane shall meet the following requirements: 1) when the waterproof layer membrane construction, treatment should be carried out detailed structure and paving the lowest elevation up by the roof; 2) gutters When gutter coil construction, Yishun gutters, gutter paving direction, along the flow direction should take joint; 3) should be parallel to the roof membrane paving. Not perpendicular to each other on the lower membrane Stones. 4) Stones roll should be smooth and straight, lap size is accurate, not distorted, wrinkles. Lap joints should be filled parts of the adhesive coating, roll solid paste. 5) should be fully adhered method uses Stones roll, flat bonded area of ??not less than 90%, facades or large slope bonded area of ??not less than 95%, after curing adhesive material thickness of not less than 1.3mm. And should reduce the short side lap roll. After construction of the waterproofing membrane should be done in a protective layer. 6) After brushing should immediately supporting adhesive paste waterproofing membrane, so as not to affect the bond quality. 7) Stones roll membrane below the air should be excluded, and roll solid paste. Fifth, product images and vision